Abstract
Silicon germanium alloys are of great interest for thin film solar cells, thanks to their adjustable bandgap and stronger absorption when compared to Si. SiGe alloys are herein epitaxially grown on (100) c-Si substrates at 175°C in a standard RF-PECVD reactor from H2/SiH4/GeH4 precursor gas mixture. A linear correlation is found between the GeH4/(SiH4+ GeH4) gas ratio and Ge content in the layer, with epitaxial growth being maintained up to 35% Ge. The alloy composition deduced from spectroscopic ellipsometry shows excellent agreement with Raman spectroscopy, glow discharge optical emission spectroscopy and SIMS-MCs+ analysis. Epitaxial SiGe strain and defects, arising from lattice mismatch, are studied as function of Ge atomic percentage by Raman and transmission electron microscopy. The SiGe electrical quality is investigated by making heterojunctions solar cells stacks, consisting of (p++)c-Si wafer/epi-Si0.63Ge0.27/(n)aSi:H, and comparing their characteristics to pure silicon equivalent devices. External quantum efficiency confirmed a short circuit current of 18.8mA/cm2 with a thin 1.9µm absorber and flat interfaces, along with a fill factor of 77.5% and an open circuit voltage of 416mV, resulting in a conversion efficiency of 6.1%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.