Abstract
AbstractArea‐selective deposition (ASD) is a forefront nanopatterning technique gaining substantial attention in the semiconductor industry. While current research primarily addresses single‐material ASD, exploring multi‐material ASD is essential for mitigating complexity in advanced nanopatterning. This study describes molybdenum hexafluoride (MoF6)‐mediated fluorination/passivation of the hydroxylated SiO2 (SiO2‒OH) at 250 °C as a new method to pacify nucleation during subsequent ZnO and TiO2 atomic layer deposition (ALD). In contrast, Al2O3 ALD is not passivated on the fluorinated SiO2 (SiO2‒F). The study further shows that Mo ALD using MoF6 and silane (1 wt% SiH4 in Ar) selectively proceeds on hydrogen‐terminated Si (Si‒H), whereas SiO2‒OH becomes fluorine‐passivated without observable Mo deposition. This enables subsequent ZnO and TiO2 ASD on Mo versus SiO2‒F, as confirmed by X‐ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Proposed growth and inhibition mechanisms highlight the importance of the metal oxide precursor in achieving selectivity. Taken together, self‐aligned Mo/ZnO and Mo/TiO2 nanoribbons are demonstrated on coplanar nanoscale Si‒H/SiO2‒OH patterns by sequentially integrating two individual ASD processes: 1) Mo ASD on Si‒H versus SiO2‒OH; and 2) ZnO or TiO2 ASD on Mo versus SiO2‒F. This work highlights the potential for this approach in new ASD systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.