Abstract
AbstractHerein we report the formulation of phenolic resin–based adhesive to join SiC substrates for a wide range of application temperatures. The formulation consists of phenolic resin as a binder and a mixture of B4C, Al2O3, Y2O3, Si, and SiO2 powders as active filler. The X‐ray diffraction, thermogravimetric analysis, porosity, and scanning electron microscopy analysis were carried out to understand the reactions occurring within this adhesive during its exposure to application temperatures. These results were also used to understand thermal stability and morphological changes that are involved in the formulated adhesive during its application. The shear strength values of lap joints of SiC substrates made with this phenolic adhesive after exposure to temperatures between 200 and 1500°C were studied to evaluate its adhesive capacity. Obtained SiC joints with this adhesive have shown an excellent lap shear strength value of 24 MPa after its cure. These joints were also found to be intact with good shear strength values of more than 5 MPa even after exposure to temperatures ranging from 200 to 1500°C. The results further confirm that the adhesive is potentially viable for joining SiC segments for their application at a wide range of temperatures in oxidative environments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.