Abstract
ABSTRACTWafer bonding is an emerging technology for fabrication of complex three-dimensional (3D) structures; particularly it enables monolithic wafer-level 3D integration of high performance, multi-function microelectronic systems. For such a 3D integrated circuits, low-temperature wafer bonding is required to be compatible with the back-end-of-the-line processing conditions. Recently our investigation on surface melting characteristics of copper nanorod arrays showed that the threshold of the morphological changes of the nano-rod arrays occurs at a temperature significantly below the copper bulk melting point. With this unique property of the copper nanorod arrays, wafer bonding using copper nanorod arrays as a bonding intermediate layer was investigated at low temperatures (400 °C and lower). 200 mm Wafers, each with a copper nanorod array layer, were bonded at 200 – 400 °C and with a bonding down-force of 10 kN in a vacuum chamber. Bonding results were evaluated by razor blade test, mechanical grinding and polishing, and cross-section imaging using a focus ion beam/scanning electron microscope (FIB/SEM). The FIB/SEM images show that the copper nanorod arrays fused together accompanying by a grain growth at a bonding temperature of as low as 200 °C. A dense copper bonding layer was achieved at 400 °C where copper grains grew throughout the copper structure and the original bonding interface was eliminated. The sintering of such nanostructures depends not only on their feature size, but also significantly influenced by the bonding pressure. These two factors both contribute to the mass transport in the nanostructure, leading to the formation of a dense bonding layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.