Low temperature and high pressure thermoelastic and crystallographic properties of SrZrO3 perovskite in the Pbnm phase

Abstract

The thermoelastic and structural properties of SrZrO3 perovskite in the Pnma (Pbnm) phase have been studied using neutron powder diffraction at 82 temperatures between 11 K and 406 K at ambient pressure, and at sixteen pressures between 0.07 and 6.7 GPa at ambient temperature. The bulk modulus, derived by fitting the equation of state to a second order Birch-Murnaghan equation-of-state, 157(5) GPa, is in excellent agreement with that deduced in a recent resonant ultrasound investigation. Experimental axial compressional moduli are in agreement with those calculated from the elastic stiffness coefficients derived by ab-initio calculation, although the experimental bulk modulus is significantly softer than that calculated. Following low temperature saturation for temperatures less than 40 K, the unit cell monotonically increases with a predicted high temperature limit in the volume expansivity of ∼2.65 × 10−5 K−1. Axial linear thermal expansion coefficients are found to be in the order αb < αc < αa for all temperatures greater than 20 K with the b axis indicating a weak, low temperature negative expansion coefficient at low temperatures. The thermoelastic properties of SrZrO3 can be approximated by a two-term Debye model for the phonon density of states with Debye temperatures of 238(4) K and 713(6) K derived in a self-consistent manner by simultaneously fitting the isochoric heat capacity and the unit cell volume. Atomic displacement parameters have been fitted to a modified Debye model in which the zero-point term is an additional refinable variable and shows the cations and anions have well separated Debye temperatures, mirroring the need for two Debye-like distributions in the vibrational density of states. The temperature dependence of the crystal structure is presented in terms of the amplitudes of the seven symmetry-adapted basis vectors of the aristotype phase that are consistent with space group Pbnm, thus permitting a direct measure of the order parameter evolution in SrZrO3. The temperature variation of the in-phase tilt, which is lost at the phase transition at 973 K, is consistent with tricritical behaviour, in agreement with published results based on high temperature crystallographic data.