Abstract
Hydrogen adsorption on clean Si(111)-7×7 and Si(100)-2×1 surfaces at low temperatures (100 K) has been investigated by a combined use of high-energy ion-beam and LEED techniques. The effect of substrate temperatures on the absolute amount of adsorbed hydrogen atoms has been measured. When hydrogen is adsorbed at room temperature, the hydrogen coverage saturates at about 1.5 monolayer (ML) for Si(111)-7×7 and at about 2.0 ML for Si(100)-2×1, respectively. However, when the substrate temperature is kept at about 100 K during adsorption, such a saturation could not be observed. The hydrogen coverage gradually increases with the increase in hydrogen exposure. After 6000 langmuir (L) exposure, the coverage is 2 or 3 times larger than those at room temperature for Si(100) and Si(111) surfaces, respectively. LEED observation shows no ordered surface structure after hydrogen adsorption.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.