Low equivalent oxide thickness metal/insulator/metal structures for DRAM application

Abstract

We have prepared metal/insulator/metal (MIM) structures with RuO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> bottom electrode and TiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> dielectric film for advanced dynamic random access memory (DRAM) technology. RuO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> films were grown by metal organic chemical vapour deposition while TiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> films were prepared by atomic layer deposition. RuO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> bottom electrode crystallizes in rutile structure and induces growth of rutile TiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> . Equivalent oxide thickness (EOT) as low as 0.39 nm and dielectric constant as high as 130 was obtained. It was found that leakage current strongly depends on either oxygen treatment after deposition or its admixture to the carrier gas during TiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> deposition. However, MIM structures under study show higher leakage current that is expected for the application (~10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-7</sup> A/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> ) in DRAM technology.