Abstract
Worldwide every year massive amount of coal fly ash is being generated as by product in the power plants which creates economic, environmental and most importantly health problems. Usually coal fly ash is used in cement production worldwide. At present, in Bangladesh, about 95 % of fly ash remains still unutilized. The alkali activation of fly ash has become a top research topic as it is possible to synthesize low cost and ecologically sound mesoporous zeolite type materials. In the present work, to the best of our knowledge, for the first time in Bangladesh, synthesis and characterization of crystalline mesoporous (H3 type hysteresis) aluminosilicate consisting of Na-P1 zeolite with a high BET specific surface area and a high pore volume from coal fly ash based on hydrothermal alkali activation technique have been successfully done. This product has versatile applications like catalysis, gas separation, water softening, water purification, gas sensing etc. The variable of alkali concentration was studied which has the notable influence on the development of the framework of the pores. The untreated coal fly ash (CFA) and the synthesized modified fly ashes (MFAs) were tested by WDS-XRF, XRD, N2 physisorption, FE-SEM, FT-IR, XPS, EDAX-mapping, particle size analysis and other technologies. The BET specific surface area, total pore volume and average pore diameter of the CFA were only 3 m2/g, 0.01 cc/g and 6.3 nm respectively based on nitrogen gas physisorption technique, whereas, after alkali activation at a specific temperature and time, and then curing, significant and promising increased values of the said parameters of 45 m2/g, 0.11 cc/g and 9.8 nm were obtained respectively. In methylene blue dye adsorption experiment, MFA showed higher adsorption capacity (23.87 mg/g).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.