Abstract
AbstractEpoxy resins with a high dielectric constant and low intrinsic thermal conductivity coefficient cannot meet the current application requirements of advanced electronic and electrical equipment. Therefore, novel fluorine‐containing liquid crystal epoxy compounds (TFSAEy) with fluorinated groups, biphenyl units, and flexible alkyl chains are first synthesized via amidation and esterification reactions. Then, 4,4′‐diaminodiphenylmethane (DDM) is used as a curing agent to prepare the corresponding fluorine‐containing liquid crystal epoxy resins. The obtained dielectric constant (ε) and dielectric loss (tan δ) values of TFSAEy/DDM at 1 MHz are 2.54 and 0.025, respectively, which are significantly lower than those of conventional epoxy resins (E‐51/DDM, 3.52 and 0.038). Additionally, the intrinsic thermal conductivity coefficient (λ) of TFSAEy/DDM is 0.36 W/(m·K), 71.4% higher than that of E‐51/DDM (0.21 W/(m·K)). Meanwhile, the corresponding elastic modulus, hardness, glass transition temperature, and heat resistance index of TFSAEy/DDM are 5.73 GPa, 0.35 GPa, 213.5°C, and 188.7°C, respectively, all superior to those of E‐51/DDM (3.68 GPa, 0.27 GPa, 107.2°C, and 174.8°C), presenting potential application in high‐heating electronic component packaging and printed circuit boards.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.