Abstract
Effect of ultrasonic shot peening (USSP) for different durations, with graded surface structures, was studied on low cycle fatigue behavior of the aluminium alloy 7075 (AA7075) at room temperature. LCF tests were conducted at different total strain amplitudes. Surface microstructures of the USSP treated specimens were characterized using X-ray diffraction and transmission-electron microscopy. No phase change was found due to USSP. Surface region of the ultrasonically shot peened sample was found to develop nanosize grains of 16-20 nm. Significant improvement was observed in LCF life of the specimen subjected to USSP for 180 seconds. However, LCF life of the sample USSPed for long duration of 300 seconds was reduced. The higher fatigue life resulting from USSP for 180 seconds, may be attributed to increased resistance of the USSPed sample against fatigue crack initiation, due to grain refinement in the surface region.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.