Abstract
In recent, ferritic stainless steels are widely used in high temperature structure because of their high resistance in thermal fatigue and low prices. Tensile and low cycle fatigue(LCF) tests on 429EM stainless steel were performed at several temperatures from room temperature to 600°C. Elastic modulus, yield stress and ultimate tensile strength(UTS) decreased with increasing temperature. Considerable cyclic hardening occurred at 200°C and 400°C. 475°C embrittlement observed could not explain this phenomenon but dynamic strain aging(DSA) observed from 200°C to 500°C could explain the hardening mechanism at 200°C and 400°C. And it was observed that plastic strain energy density(PSED) was useful to predict fatigue life when large cyclic hardening occurred. Fatigue life using PSED over elastic modulus could be well predicted within 2X scatter band at various temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.