Low Cost Fabrication of 2G Wires for AC Applications

Abstract

Ink-jet printing has been demonstrated as an adaptable technology for printing YBCO filaments using a Metal Organic (MO) YBCO precursor. The technology was demonstrated using AMSC's proprietary metal organic TFA-based YBCO precursor and a commercial piezoelectric print-head on RABiTS templates. Filaments with a width of 100 um and spacing of 200 um were successfully printed, decomposed and processed to YBCO. Critical currents of {approx} 200 A/cm-w were achieved in a series of filaments with a 2 mm width. The single nozzle laboratory printer used in the Phase 1 program is capable of printing {approx} 100 um wide single filaments at a rate of 8-10 cm/sec. The electrical stabilization of filaments with a Ag ink was also evaluated using ink-jet printing. The overall objective of the Phase 1 Project was the evaluation and demonstration of inkjet-printing for depositing YBCO filaments on textured templates (RABiTS, IBAD, ISD, etc. substrates) with properties appropriate for low loss ac conductors. Goals of the Phase 1 program included development of an appropriate precursor ink, demonstration of the printing process, processing and characterization of printed YBCO filaments and evaluation of the process for further development.