Abstract
AbstractHot‐dip Zn55Al‐coated steel samples have been exposed for up to 6 years at 11 different weathering sites, including marine, marine‐industrial, acid‐rain and dry atmospheres. From the mass loss measurements, Zn55Al metallic coating showed globally long‐term good corrosion resistance in all weathering conditions compared with hot‐dip Zn‐0.2Al‐coated steel (Z). Yet, weaker performance was observed on Zn55Al in high SO2 polluted atmosphere, particularly when combined with seawater aerosols. This is explained by a more acidic surface condition linked to high SO2. Although the extent of corrosion in this phase was different at the different sites, the final corrosion products formed after 6 years were rather similar at all sites. This consists of hydrous aluminium sulphate or hydrous aluminium hydroxy sulphate and, probably also a smaller amount of sulphate‐containing zinc corrosion products or Al/Zn products.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.