Abstract

The high operating voltage of a spinel LiNi0.5Mn1.5O4 (LNMO) cathode leads to electrolyte decomposition and accelerated deterioration of the electrode/electrolyte interface in lithium-ion cells. Aggressive side reactions prevent long-term cycling and hinder its practical application. Advanced characterization shows that the high-voltage operation makes the graphite anode react with the electrolyte, particularly with the lithium salt in the electrolyte, resulting in massive active lithium inventory loss and capacity fade. The side reactions at the graphite are identified as the main culprit for the LNMO/graphite full cell decay. Here, we demonstrate that an artificial solid-electrolyte interface layer consisting of an ultra-thin Al2O3 film, generated via atomic layer deposition (ALD) at the graphite surface, can successfully isolate the graphite from the electrolyte and inhibit the undesired reactions. Consequently, the capacity and cycling stability of the LNMO/graphite cell are drastically improved. After 300 cycles, the capacity retention of LNMO/graphite cell increases from 57.7% to 98.6% with the ALD-coated graphite. Our findings provide valuable insights into the LNMO/graphite cell degradation and suggest a simple and robust, yet highly effective, approach for the practical viability of high-voltage lithium-ion batteries.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.