Abstract
Local structural arrangements and stabilities of oxygen and hydrogen-related defects in proton-conducting LaP3O9 were studied using first principles calculations. When an oxygen was removed from LaP3O9, the crystal lattice was significantly distorted. Resulting structural arrangements considerably depended on the oxygen deficient site, and phosphate ions tended to condense by sharing a corner oxygen of PO4 tetrahedra. On the other hand, when a proton was introduced, the proton was located at the interstitial sites positioned approximately 1Å away from the nearest oxygen forming an O–H bond. The LaP3O9 lattice was only slightly distorted even after introduction of an interstitial proton. Based on the calculation results, the stabilities of the defects under moisturized conditions was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.