Patterned Few Layers Graphene (FLG) films were grown by local solid phase epitaxy from nickel silicide supersaturated with carbon. The process was realised by annealing of thin Ni films deposited on the carbon-terminated surface of 6H-SiC semi-insulating wafer followed by wet processing to remove the resulting nickel silicide. Raman spectroscopy was used to investigate both the formation and subsequent removal of nickel silicide during processing. Characterisation of the resulting FLG films was carried out by Raman spectroscopy and Atomic Force Microscopy (AFM). The thickness of the final FLG film estimated from the Raman spectra varied from 1 to 3 monolayers for initial Ni layers varying from 3 to 20 nm thick. AFM observations revealed process-induced surface roughening in FLG films, however, electrical conductivity measurements by Transmission Line Model (TLM) structures confirmed that roughness does not compromise the film sheet resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.