Abstract
AbstractAll‐solid‐state batteries with conversion‐type cathodes promise to exceed the performance of lithium‐ion batteries due to their high theoretical specific energy and potential safety. However, the reported performance of solid‐state batteries is still unsatisfactory due to poor electronic and ionic conduction in the composite cathodes. Here, in situ formation of active material as well as highly effective ion‐ and electron‐conducting paths via electrochemical decomposition of Li6PS5Cl0.5Br0.5 (LPSCB)/multiwalled carbon nanotube mixtures during cycling is reported. Effectively, the LPSCB electrolyte forms a multiphase conversion‐type cathode by partial decomposition during the first discharge. Comprehensive characterization, especially operando pressure monitoring, reveals a co‐redox process of two redox‐active elements during cycling. The monolithic LPSCB‐based cell shows stable cycling over 1000 cycles with a very high capacity retention of 94% at high current density (0.885 mA cm−2, ≈0.7 C) at room temperature and a high areal capacity of 12.56 mAh cm−2 is achieved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.