Abstract
Densification of alumina coated with a MgO‐Al2O3‐SiO2 (MAS) glass was investigated from 1400° to 1460°C. Spinel was observed to form at the liquid‐alumina interface, whereas mullite crystallized uniformly in the liquid. Spinel and mullite crystallization kinetics were accelerated by smaller alumina particle size. Mullite and spinel crystallization retarded densification by forming a percolating network. Boron doping suppressed spinel formation, and thus alumina sintered to higher densities at low temperature. The concept of glass basicity is proposed as a useful guide for selecting dopants for low‐temperature sintering.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.