Abstract

Graphene dispersions were prepared using the liquid phase exfoliation method with three different surfactants. One surfactant was used from each of the surfactant types, anionic, cationic, and non-ionic; those used, were sodium dodecylbenzene sulfonate (SDBS), cetyltrimethylammonium bromide (CTAB) and polyvinylpyrrolidone (PVP), respectively. Raman spectroscopy was used to investigate the number of layers and the nature of any defects present in the exfoliated graphene. The yield of graphene was found to be less with the non-ionic surfactant, PVP. The deconvolution of 2D peaks at ~2700 cm−1 indicated that graphene prepared using these surfactants resulted in sheets consisting of few-layer graphene. The ratio of intensity of the D and G bands in the Raman spectra showed that edge defect density is high for samples prepared with SDBS compared to the other two, and is attributed to the smaller size of the graphene sheets, as shown in the electron micrographs. In the case of the dispersion in PVP, it is found that the sizes of the graphene sheets are highly sensitive to the concentration of the surfactant used. Here, we have made an attempt to investigate the local density of states in the graphene sheets by measuring the tunnelling current–voltage characteristics. Graphene layers have shown consistent p-type behaviour when exfoliated with SDBS and n-type behaviour when exfoliated with CTAB, with a larger band gap for graphene exfoliated using CTAB. Hence, in addition to the known advantages of liquid phase exfoliation, we found that by selecting suitable surfactants, to a certain extent it is possible to tune the band gap and determine the type of majority carriers.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call