Abstract
NiAl-Ni 3Al intermetallic composites (IC) and intermetallic matrix composites (IMC) with TiC and WC reinforcement were laser clad to increase the liquid impact erosion resistance of AISI 420 Martensitic stainless steel. Laser process parameter optimisation and pre- and post-heat treatment of the laser clad specimens were carried out to minimise porosity and sensitivity to crack formation. The coatings were characterised by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS). The erosion resistance of the substrate material at a water droplet exit velocity of up to 150 m/s was improved from 116.9 to 838.7 min/mm 3 for the nickel aluminide IC coating and from 855 to 1446 min/mm 3 for the IMC coating with TiC and WC reinforcement. The pseudo-elasticity combined with the high work hardening ability was attributed to the excellent erosion resistance of nickel aluminide IC coatings. The IMC coatings with ceramic reinforcement extended significantly the initial resistance against liquid impact erosion. However, once damage occurred the erosion accelerated rapidly. No direct correlation could be established between the erosion resistance and the mechanical properties. The influence of hardness, elastic modulus, strain-hardening coefficient and the reversible penetration ratio on the erosion resistance was discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.