Abstract
As an extension of our previous studies concerning the free radical copolymerisation of 25,26,27-tripropoxy-28-(4-vinyl-benzyloxy)- p-tert-butylcalix[4]arene ( 3) with styrylic monomers, we report herein on the synthesis and characterisation of new terpolymers derived from 3, styrene and divinylbenzene, having nominal crosslinking degrees ranging from 4% to 40% wt. The terpolymers exhibited good thermal stabilities (DSC) and were prepared in good yields. Depending on the reaction conditions (dilution degree and aqueous phase to porogen ratio), materials with identical nominal crosslinking but otherwise differentiated morphologies and swelling abilities were obtained. In a related study, the radical polymerisation of styrene was carried out in the presence of a novel calix[4]arene derivative 4, bearing two distal benzyl–vinyl groups in the lower rim. It is shown that, albeit the presence of two phenolic groups within the calixarene moiety which could have functioned as inhibitors of the free radical polymerisation, the macrocycle was able to take part in the copolymerisation reaction, yielding new soluble and crosslinked polymers. In both cases, no pendant vinyl groups were found in the polymeric materials. The probable mechanisms underlying their formation are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.