Abstract

ABSTRACTSilicon-on-insulator films have been formed using a 20 mm by 1 mm line-source electron beam, with sample sweep speeds of 100–500 cm/sec and peak beam power densities up to 75 kW/cm2. Films were formed over 1 and 2 μm thick SiO2 isolating layers on 4°C diameter Si<100> wafers, with stripe openings of 5 to 100 μ width for seeding the crystallization from the substrate. Films consisted of Si layers from 0.4 to 1.0 μm thickness, with a capping layer of 2 μm SiO2. By sweeping the beam parallel to the long axis of the seed openings, smooth, oriented films were obtained, with low-angle grain boundaries confined to midway between seed openings. Best results were obtained for ≲ 50 μm spacing between seed openings.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.