Abstract
Global photoluminescence (PL) and spatially resolved scanning tunneling microscopy (STM) luminescence are compared for thick Cu2O films grown on Au(111). While the PL data reveal two peaks at 750 and 850 nm, assigned to radiative electron decays via localized gap states induced by O vacancies, a wide-band emission between 700 and 950 nm is observed in STM luminescence. The latter is compatible with cavity plasmons stimulated by inelastic electron tunneling and contains no spectral signature of the Cu2O defects. The STM luminescence is nonetheless controlled by O vacancies that provide inelastic excitation channels for the cavity plasmons. In fact, the emission yield sharply peaks at 2.2 V sample bias, when tip electrons are resonantly injected into O defect states and recombine with holes at the valence-band top via plasmon stimulation. The spatially confined emission centers detected in photon maps of the Cu2O films are therefore assigned to excitation channels mediated by single or few O vacancies in the oxide matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.