Abstract
This study investigates the microstructure of the visible diffusion zone formed in low carbon steel pack cyanided using processed cassava leaves. Standard parts machined from low carbon steel were pack cyanided by high temperature in-situ diffusion of nascent carbon and nitrogen into austenite. Formation of a visible diffusion zone was confirmed after observation with a Reichert-Jung Polyval optical microscope coupled with Zeiss AxioCam ICc 1 camera. High magnification Scanning Electron Microscope (SEM) imaging of the visible diffusion zone was done with a CamScan Series 2 scanning electron microscope. The zone was found variable in depth as measured from a representative position. The structure of all samples consists of ferrite and pearlite as determined by optical and SEM examination. Resulting products were thus both tough and hard suitable for service environments requiring high resistance to both wear and impact failure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.