Abstract
Thermal behavior of commercial PVC cable insulation both before and after extraction of plasticizers, fillers and other agents were tested by TG/DTG and DSC during heating in the range 20-800°C in air. The ultrasound enhanced hexane extraction and dissolution in THF with subsequent precipitation of PVC were used to prepare 'extracted' and 'precipitated' samples. The total mass loss measured for the 'non-treated', 'extracted' and 'precipitated' PVC samples was 71.6, 66.6 and 97%, respectively. In the temperature range 200-340°C the release of dioctylphthalate, HCl and CO2was observed by simultaneous TG/FTIR. From TG results measured at different heating rates (1.5, 5, 10, 15 K min-1) in the range 200-340°C the non-isothermal kinetics of the PVC samples degradation was determined. Activation energy values of the thermal degradation processes calculated by ASTM E 698 method, for 'non-treated', 'extracted' and 'precipitated' PVC samples were 174.6±17 kJ min-1, 192.8±19 kJ min-1, 217.1±20 kJ min-1, respectively. These kinetic parameters were used for the lifetime simulation of the materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.