Abstract
AbstractThe timescale at which ductile failure occurs in loaded glassy polymers can be successfully predicted using the engineering approach presented in a previous publication. In this paper the influence of progressive physical ageing on the plastic deformation behaviour of unplasticised poly(vinyl chloride) (uPVC) is characterised and incorporated in the existing approach. With the modification it is possible to quantitatively predict long‐term failures which show a so‐called endurance limit. The predictions are compared with failure data of uPVC specimens which were subjected to constant or dynamic loads. In dynamic loading conditions a second type of failure mode was observed: fatigue crack growth. A brief study on the influence of the frequency and stress ratio of the applied stress signal shows that crack growth failure is not expected to occur within experimentally reasonable timescales for constant loading conditions.magnified image
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.