Abstract
In order to solve the problem of device miniaturization, it is urgent to develop high performance medium K materials. A series of (1-x) Ba3Ti4Nb4O21-x Li2WO4 ceramics (1-xBTN-xLW, x=12, 15, 17 and 20 mol%) were fabricated by soild-state reaction method. Li2WO4 as the effective sintering aids (~640°C) not only promoted ceramic densification and also decreased the temperature to 925°C. Among them, the 0.83BTN-0.17LW ceramic achieved best microwave performance with ε r~21.85, Q×f~10534 GHz, τ f ∼-7.78 ppm/°C. Especially, the second phase BaWO4 played major factor on microwave performance, making high K materials transfer into medium K materials and decrease the loss. More encouragingly, the temperature coefficient τ f was near zero. The above outstanding results signified that the 0.83BTN-0.17LW ceramic was expected to be a candidate material for LTCC miniaturized devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.