Abstract
Abstract In the present study the Li diffusivity in nanostructured samples of two glass forming model systems, spodumene (LiAlSi2O6) and lithium metaborate (LiBO2), was examined using 7Li nuclear magnetic resonance (NMR) spin-lattice relaxometry and dc conductivity measurements. The nanostructured samples were prepared by high-energy ball milling of the respective crystalline starting material on the one hand and the corresponding glass on the other hand. The diffusivity of the glass exceeds that of the crystalline sample for both systems. However, when the crystalline samples are mechanically treated by ball milling the diffusivity is enhanced. Nevertheless, the diffusivity of these nanocrystalline samples remains lower than that of the corresponding glass. Surprisingly, when the glassy samples are treated in the same way the diffusivity decreases. After sufficiently long milling times the diffusivity of these nanoglassy samples approaches that of the nanocrystalline samples. This convergence effect seems to be due to structural relaxation processes as is suggested by supplementary infrared spectroscopy and 27Al, 12B magic angle spinning NMR measurements.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.