Abstract
A novel three-dimensional (3D) hierarchical porous cobalt oxide (Co3O4) architecture was first synthesized through a simple, cost-effective and environmentally friendly leaf-templated strategy. The Co3O4 nanoparticles (30–100nm) with irregular shapes were interconnected with each other to form a 3D multilayer porous network structure, which provided high specific surface area and numerous electrocatalytic active sites. Subsequently, Co3O4 was successfully utilized as direct electrochemical sensing interface for non-enzymatic detection of H2O2 and glucose. By using chronoamperometry, the current response of the sensor at +0.31V was linear with H2O2 concentration within 0.4–200μM with a low limit of detection (LOD) of 0.24μM (S/N=3) and a high sensitivity of 389.7μAmM−1cm−2. Two linear ranges of 1–300μM (with LOD of 0.1μM and sensitivity of 471.5μAmM−1cm−2) and 4–12.5mM were found at +0.59V for glucose. In addition, the as-prepared sensor showed excellent stability and anti-interference performance for possible interferents such as ascorbic acid, uric acid, dopamine, acetaminophen and especially 0.15M chloride ions. Similarly, other various metal oxide nanostructures may be also prepared using this similar strategy for possible applications in catalysis, electrochemical sensors, and fuel cells.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.