Abstract
Electrocaloric refrigeration utilizing ferroelectrics has recently gained tremendous attention because of the urgent demand for solid-state cooling devices. However, the low room-temperature electrocaloric effect and narrow operation temperature window hinder the implementation of lead-free ferroelectrics in high-efficiency cooling applications. In this work, chemical engineering and thick-film architecture design strategies were integrated into a BaTiO3-based system to resolve this challenge. Novel environmental-friendly Ba(Zr0.20Ti0.80)O3-Ba(Sn0.11Ti0.89)O3 (BZT-BST) bilayer films of ∼13 μm in single-layer thickness were prepared by the tape casting process. A giant adiabatic temperature change, Δ T ∼ 5.2 K, and a large isothermal entropy change, Δ S ∼ 6.9 J kg-1 K-1, were simultaneously achieved at room temperature based on the direct measurements, which are much higher than those reported previously in many lead-free ferroelectrics. Moreover, the BZT-BST thick films exhibited a remarkably widened operation temperature range from about 10 to 60 °C. These outstanding properties were mainly attributed to the multiphase coexistence near room temperature, relaxor ferroelectric characteristics, and improved electric-field endurance of the bilayer thick films. This work provides a guideline for the development of environment-friendly electronic materials with both ultrahigh and stable electrocaloric performance and will broaden the application areas of lead-free ferroelectrics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.