Abstract
ABSTRACTAl-Ga interdiffusion, carbon acceptor diffusion, and hole reduction were studied in carbondoped Al0.4Ga0.6As/GaAs superlattices (SL). Al-Ga interdiffusion was found to be most prominent for Ga-rich annealing, with the hole concentrations in the SL almost intact during annealing. For As-rich annealing, the interdiffusivity values, DAI.Ga, are in approximate agreement with those predicted by the Fermi-level effect model, and the hole concentrations in the SL decreased dramatically after annealing. By analyzing the measured hole concentration profiles, it was found that both carbon acceptor diffusion and reduction have occurred during annealing, with both depending on As4 pressure values to the one quarter power. These As4 pressure dependencies indicate that carbon diffuses via the interstitial-substitutional mechanism while hole reduction is governed by a precipitation mechanism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.