Abstract
Polylactic acid (PLA) is a biodegradable, biocompatible and non-toxic biopolymer with good mechanical properties, and is commonly used for the additive manufacture of PLA-based biomedical devices. Such devices are available in a range of sizes and thicknesses, with smaller devices capable of being realised via additive manufacturing in just a few layers. Due to their thermal history and thermal degradation, the thermal, molecular weight and mechanical properties of each layer was different when the raw material was melted, and the in-course layer was deposited to the previous layer. This study investigated the effect of the number of layers on mechanical, thermal and molecular weight properties, and the relationship between them. Material extruded ISO 527–2 type 5A specimens with 1-, 2-, 3-, 4-, 5-, 7- and 10-layers were prepared with the cutting die. Results indicated that the degree of crystallinity was found to decrease from 8% to 0.5% with an increasing number of layers. This was likely due to different cooling rates, where the molecular weight was lowest for 1-layer and increased with the increasing number of layers until it almost reached that of the bulk material. Additionally, ultimate tensile strength and strain increased with an increasing number of layers, while Young's Modulus decreased due to heterogeneous material structure. Of all obtained results, there was no significant difference between 5- and 10-layer in terms of mechanical and thermal properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.