Abstract

AbstractLead sulfide (PbS) presents large potential in thermoelectric application due to its earth‐abundant S element. However, its inferior average ZT (ZTave) value makes PbS less competitive with its analogs PbTe and PbSe. To promote its thermoelectric performance, this study implements strategies of continuous Se alloying and Cu interstitial doping to synergistically tune thermal and electrical transport properties in n‐type PbS. First, the lattice parameter of 5.93 Å in PbS is linearly expanded to 6.03 Å in PbS0.5Se0.5 with increasing Se alloying content. This expanded lattice in Se‐alloyed PbS not only intensifies phonon scattering but also facilitates the formation of Cu interstitials. Based on the PbS0.6Se0.4 content with the minimal lattice thermal conductivity, Cu interstitials are introduced to improve the electron density, thus boosting the peak power factor, from 3.88 μW cm−1 K−2 in PbS0.6Se0.4 to 20.58 μW cm−1 K−2 in PbS0.6Se0.4−1%Cu. Meanwhile, the lattice thermal conductivity in PbS0.6Se0.4−x%Cu (x = 0–2) is further suppressed due to the strong strain field caused by Cu interstitials. Finally, with the lowered thermal conductivity and high electrical transport properties, a peak ZT ~1.1 and ZTave ~0.82 can be achieved in PbS0.6Se0.4 − 1%Cu at 300–773K, which outperforms previously reported n‐type PbS.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.