Lateral interactions in the thermal desorption of H 2 from clean Cu/Ni(110) alloy surfaces

Abstract

The adsorption of hydrogen on a clean Cu10%/Ni90% (110) alloy single crystal was studied using flash desorption spectroscopy (FDS), Auger electron spectroscopy (AES), and work function measurements. Surface compositions were varied from 100% Ni to 35% Ni. The hydrogen chemisorption on a-surface of 100% nickel revealed strong attractive interactions between the hydrogen atoms in accordance with previous work on Ni(100). Three desorption states ( β 1, β 2 and α) appeared in the desorption spectra. The highest temperature ( α) state was occupied only after the initial population of the β 2-state. As the amount of copper was increased in the nickel substrate, desorption from the higher energy binding α-state was reduced, indicating a decrease in the attractive interactions among hydrogen atoms. The hydrogen coverage at saturation was not affected by the addition of copper to the nickel substrate until the copper concentration was greater than 25% at which a sharp reduction in saturation coverage occurred. This phenomenon was apparently due to the adsorption of hydrogen on Ni atoms followed by occupation of NiNi and CuNi bridged adsorption sites, while occupation of CuCu sites was restricted due to an energy barrier to migration.