Abstract
Annealed high speed steels for making tools such as W6Mo5Cr4V2, W9Mo3Cr4V1, W18Cr4V were treated with 5 kw continuous adjusting CO2 laser. By controlling laser- processing parameters, we achieved variable datum about the depth and hardness of the surface hardening layer of the samples. The relationship between the depth of hardening layer and laser processing parameters were studied with microhardness meter, scanning electronic microscope. The results showed that the sample's micro organization was markedly fined, dislocation and twin crystal subconstruction was strikingly increased, its hardness was obviously higher than that of general heat treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.