Abstract
AbstractThe structure and phase composition of HAp coatings deposited onto Ti6Al4V coupons (50x20x2mm) by atmospheric plasma spraying (APS) were studied by laser‐Raman spectroscopy, 31P‐ and 1H‐MAS‐NMR and 2D‐31P/1H HETCOR‐CP‐NMR spectroscopy, and XRD with Rietveld refinement. The samples investigated comprised APS HAp coatings with and without a TiO2 bond coat as well as coatings incubated for different lengths of time (up to 12 weeks) in simulated body fluid (SBF) under physiological conditions. In APS coatings the presence of a bond coat increased the proportion of well‐ordered crystalline HAp at the expense of distorted apatite‐like structures such as oxyHAp and oxyapatite, and thermal decomposition products such as tricalcium phosphate (TCP) and tetracalcium phosphate (TTCP), and also decreased the amount of amorphous calcium phosphate (ACP). Incubation in SBF further advanced the proportion of crystalline HAp since the disordered structures, the thermal decomposition products, and ACP exhibit substantially higher solubility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.