Abstract
This work investigates the film removal properties of 30nm thick Indium Tin Oxide (ITO) thin films, on flexible polyethylene terephthalate (PET) substrates, using 355, 532 and 1064nm nanosecond pulses (ns), and 343 and 1064nm femtosecond pulses. The ablation threshold was found to be dependent on the applied wavelength and pulse duration. The surface topography of the laser induced features were examined using atomic force microscopy across the range of wavelengths and pulse durations. The peak temperature, strain and stress tensors were examined in the film and substrate during laser heating, using finite element computational methods. Selective removal of the thin ITO film from the polymer substrate is possible at all wavelengths except at 266nm, were damage to substrate is observed. The damage to the substrate results in periodic surface structures (LIPPS) on the exposed PET, with a period of twice the incident wavelength. Fragmented crater edges are observed at all nanosecond pulse durations. Film removal using 1030nm femtosecond pulses results in clean crater edges, however, minor 5nm damage to the substrate is also observed. The key results show that film removal for ITO on PET, is through film de-lamination across all wavelengths and pulse durations. Film de-lamination occurs due to thermo-elastic stress at the film substrate interface region, as the polymer substrate expands under heating from direct laser absorption and heat conduction across the film substrate interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have