Laser conditioning and multi-shot laser damage accumulation effects of HfO 2/SiO 2 antireflective coatings

Abstract

Laser conditioning effects of the HfO 2/SiO 2 antireflective (AR) coatings at 1064 nm and the accumulation effects of multi-shot laser radiation were investigated. The HfO 2/SiO 2 AR coatings were prepared by E-beam evaporation (EBE). The single-shot and multi-shot laser induced damage threshold was detected following ISO standard 11254-1.2, and the laser conditioning was conducted by three-step raster scanning method. It was found that the single-shot LIDT and multi-shot LIDT was almost the same. The damage mostly >80% occurred in the first shot under multi-shot laser radiation, and after that the damage occurring probability plummeted to <5%. There was no obvious enhancement of the laser damage resistance for both the single-shot and multi-shot laser radiation of the AR coatings after laser conditioning. A Nomarski microscope was employed to map the damage morphology, and it found that the damage behavior is defect-initiated for both unconditioned and conditioned samples.