Abstract
Over the past decade, researchers have demonstrated much interest in laser cladded metal matrix composite coatings for its good wear resistance, corrosion resistance and high temperature properties. The effects of RE on the microstructure and properties of laser coatings have also got more and more attention. In this paper, in situ Fe-NbC composite coatings with different CeO2 addition were produced on die steel by laser cladding. The formation mechanism of NbC particles was analyzed. The effects of RE on microstructure and micro-hardness of coatings were investigated. It was revealed that larger NbC particles with hard edges formed around Nb particles, and smaller flocculent NbC particles formed by the chemical reaction of Nb and solid graphite in the molten pool. CeO2 plays important roles in reducing micro-porosities, refining grains, and improving the precipitation of NbC. Therefore, the average micro-hardness and its smoothness from the top to the bottom of the coating were improved after adding CeO2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.