Abstract

The increase of the lifetime of modern single crystalline (SX) turbine blades is of high economic priority. The currently available repair methods using polycrystalline cladding of the damaged area do not address the issue of monocrystallinity and are restricted to few areas of the blade. The tip area of the blade is most prone to damage and undergoes the most wear, erosion and cracking during its lifetime. To repair such defects, the common procedure is to remove the whole tip with the damaged area and rebuild it by applying a polycrystalline solidification of the material. The repair of small cracks is conducted in the same way. To reduce repair cost, the investigation of a manufacturing process to repair these cracked areas while maintaining single-crystal solidification is of high interest as this does not diminish material properties and thereby its lifetime. To establish this single-crystal solidification, the realization of a directed temperature gradient is needed. The initial scope of this work is the computational prediction of the temperature field that arises and its verification during the process. The laser cladding process of CMSX-4 substrates was simulated and the necessary parameters calculated. These parameters were then applied to notched substrates and their microstructures analyzed. Starting with a simulation of the temperature field using ANSYS®, a process to repair parts of single crystalline nickel-based alloys was developed. It could be shown that damages to the tip area and cracks can be repaired by establishing a specific temperature gradient during the repair process in order to control the solidification process.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.