Laser 열처리를 이용한 FeMn/NiFe 박막의 자화 반전

Abstract

We have studied local magnetization reversal and magnetic properties induced by Laser annealing method in the strip-patterned Ta/NiFe/FeMn/Ta and Ta/NiFe/FeMn/NiFe/Ta multilayers fabricated by ion-beam deposition. The films were exposed to the emission of the DPSS (Diode Pumped Solid State, Nd:YAG) laser under 600 G. The laser beam intensity increased up to 440 mW. When the laser illuminated the patterned film with the power of above 200 m W, the intensity of MR peak located in +87 Oe shrunk. A new MR peak was generated at -63 Oe. When the laser power is 400 mW, the location of positive MR peak(Hex/) was changed slightly from +87 Oe to +76 Oe, and the MR ratio was decreased from 0.9% to 0.1 %. On the other hand, the new (negative) MR peak shifted from -63 Oe to -80 Oe, with the MR ratio increased up to 0.3%. As the illuminated area expanded, the intensity of opposite MR peak increased and it of negative MR peak decreased. This proved that the local reversal of exchange biasing should be realized by laser annealing.