Abstract
The intrinsic stress of tetrahedral amorphous carbon film as a function of annealing temperature is investigated. The film was deposited using the filtered cathodic vacuum arc technique and subsequently annealed at various temperatures. The stress is determined by Stoney’s equation using surface profilometry, and the microstructure is studied using atomic force microscopy, visible and ultraviolet Raman spectroscopy. It is found that as the annealing temperature increases the film stress decreases slowly up to 500 oC and then falls quickly at 600 oC. It is interesting to note that at this temperature sp3 fraction retains while sp2 clustering begins, which contributes to the sharp decrease in the stress.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Metastable and Nanocrystalline Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.