Abstract
Magnetocaloric effect (MCE) of RMn2 (R=Tb, Dy, Ho, Er) compounds are investigated. TbMn2 and DyMn2 crystallize in cubic Laves phase structure (C15 type), whereas HoMn2 and ErMn2 crystallize in hexagonal Laves phase structure (C14 type). For TbMn2 compound, the field-induced metamagnetic transition accompanying a spontaneous cell volume expansion is observed (inverse MCE), which leads to a large positive value (8.3Jkg−1K−1) of magnetic entropy change around 36K under the field change of 0–1T, while the maximal values of magnetic entropy change (ΔSM) and the refrigerant capacity (RC) for other RMn2 (R=Dy, Ho, Er) compounds are −15.7, −18.4, −25.5Jkg−1K−1 and 403.6, 404.3, 316.0Jkg−1 around their TC with negligible thermal and magnetic hysteresis loss for the field change of 0–5T, respectively. The results suggest that RMn2 (R=Dy, Ho, Er) may be appropriate candidates for magnetic refrigerant working at low temperature region 10–80K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.