Abstract
The crystal structure, phase transition and exchange bias effect in induction melted polycrystalline ribbons of Ni55Mn19Al24Si2 have been studied using room temperature x-ray diffraction (XRD), differential scanning calorimetry (DSC) and magnetic measurements. The sample was found to show structural transformation temperatures such as austenite start (As)=306K, austenite finish (Af)=316K, martensite start (Ms)=305K and martensite finish (Mf)=294K all above room temperature. The room temperature structure evaluated as orthorhombic 14M with lattice parameters a=4.14Å, b=29.84Å, and c=5.72Å. Importantly at ~2K, the sample showed a large exchange bias field of about 2520Oe, which is the maximum value ever reported among the Heusler alloy samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.