Large-Area n-Type PERT Solar Cells Featuring Rear p+ Emitter Passivated by ALD Al2 O3

Abstract

We present large-area n-type PERT solar cells featuring a rear boron emitter passivated by a stack of ALD Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> and PECVD SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> . After illustrating the technological and fundamental advantages of such a device architecture, we show that the Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> stack employed to passivate the boron emitter is unaffected by the rear metallization processes and can suppress the Shockley-Read-Hall surface recombination current to values below 2 fA/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> , provided that the Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> thickness is larger than 7 nm. Efficiencies of 21.5% on 156-mm commercial-grade Cz-Si substrates are demonstrated in this study, when the rear Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> passivation is applied in combination with a homogeneous front-surface field (FSF). The passivation stack developed herein can sustain cell efficiencies in excess of 22% and V <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">oc</sub> above 685 mV when a selective FSF is implemented, despite the absence of passivated contacts. Finally, we demonstrate that such cells do not suffer from light-induced degradation.