Large actuation strain over 0.3% in periodically orthogonal poled BaTiO3 ceramics and multilayer actuators via reversible domain switching

Abstract

Lead titanate zirconate (PZT) ceramics based piezoelectric actuators always suffer from small output strains (typically 0.1%–0.15%) and have recently been criticized for the toxicity problem of the high-concentration lead. In our recent work (Li et al 2017 J. Appl. Phys. 122 074103), we realized large local actuation strain nearly 0.6% in a periodically orthogonal poled (POP) PZT ceramics via reversible domain switching. In this work, we applied the POP method to barium titanate (BT) ceramics and proposed a specially designed multilayer actuator which can output large uniform strain. The simple tetragonal structure of BT ceramics makes it easier to understand the mechanism of reversible domain switching in POP ceramics and its lead-free characteristic is more promising. Firstly, a POP BT ceramic piece was fabricated and the actuation testing results show that local large actuation strain of 0.36% can be obtained under a field of 2 kV mm−1 at 0.1 Hz. However, the actuation strain is non-uniform along the period direction, varying from 0.22% to 0.36%. Then, to output uniform large strain, a four-layer actuator based on the POP BT ceramics was designed and fabricated in which only the in-plane poled regions of the adjacent layers were bonded. Results show that the output strain turns to be uniform in this way, which is 0.34% under 2 kV mm−1, resulting in a very high large-signal (=Smax/Emax) of 1700 pm V−1. The large actuation strain is very stable and keeps unchanged after 20k cycles of operation. It drops quickly with the increasing frequency and is stabilized at 0.18% above 1.0 Hz. Finally, bipolar field testing was conducted on the POP BT based actuator. Results show that the actuator shows electrostriction-like symmetric bipolar actuation behavior with the repeatable actuation strain of 0.3% under 2 kV mm−1. This work may provide a feasible solution to low frequency, large-strain lead-free piezoelectric actuation.