Abstract
The aim of the study was to evaluate some properties of modern orthodontic plastic brackets. Seven bracket brands [Aesthetik-Line (AL), Avalon (AV), Brillant (BR), Elegance (EL), OrthoFlex (OF), Silkon Plus (SL), and Spirit MB (SP)] were included in the study. The properties tested were chemical composition, base morphology, slot roughness, Vickers hardness (VH), and shear bond strength (SBS) with enamel.According to the results, the brackets were composed of polyurethane (AV and OF), polyoxymethylene (BR), and Ca-Al-silicate fibre glass-reinforced polycarbonate (AL, EL, SL, and SP). Metallic slots were composed of austenitic stainless steel (EL and SP) and Ag-Cu alloy (AV). The base morphology exhibited distinct designs, employing parallel retentive canals (AV, EL, and OF) or round-angled square protrusions with major retentive elements (AL, BR, and SP) or a combination of both (SL). The SP metallic slot demonstrated the lowest Sz values. No significant differences were found in VH among the brackets before water immersion (19.6-16.9 VH). After 12 weeks immersion, the brackets showed a significant hardness reduction (16.6-12.9 HV). SBS ranged between 111 and 193 N (8-14 MPa) for all brackets, except from SP (59 N/5 MPa). The predominant failure mode was mixed adhesive and cohesive. Most of the plastic brackets presented a base structure capable of adequate bonding to enamel, regardless of their differences in composition. Slot roughness showed differences among groups. All the brackets demonstrated plasticization after prolonged water storage.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.