Abstract
The corrosion of superheater tube material in straw-fired boilers was investigated in the laboratory. Metal test elements of boiler tube steel (X20CRMV121 and AISI 347FG) were covered with synthetic (KCl and/or K2SO4) and real deposits, and exposed to a synthetic flue gas (6 vol % O2, 12 vol % CO2, 400 ppmv HCl, 60 ppmv SO2, balance N2) in 550 °C electrically heated ovens. Exposure times from 1 week to 5 months were used. The corrosion of the metal test elements was, in general, quite uniform, and the corrosion products consisted mainly of oxides of iron and chromium. All test elements covered with KCl suffered from minor internal attack, and some elements had severe pits with chlorine found in the pit. A dense layer of potassium sulfate and iron oxide was found adjacent to the metal oxide layers on all the metal test elements covered with a deposit containing KCl. The layer had a characteristic structure, with iron oxide threads in a dense potassium sulfate matrix. A mechanism for chlorine corrosion is s...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.