Abstract
Background: The acceptance of compostable plastic packaging in industrial composting plants is not universal despite available certification due to the persistence of plastic residues after composting. To better understand this discrepancy, this study compared the disintegration rates of two blends designed for rigid packaging (polylactic acid based) and soft packaging (polybutylene succinate based) in lab-scale composting tests and in an industrial composting plant. Methods: A lab-scale composting test was conducted in triplicates according to ISO 20200 for 4, 8 and 12 weeks to check the disintegration potential of the blends. Duplicate test material were then exposed in the compost pile of an industrial composting plant for a duration of 3 weeks and compared with a supplementary lab-scale test of the same duration. Results: The rigid packaging samples (1 mm thickness) retained on average 76.4%, 59.0% and 55.7% of its mass after 4, 8 and 12 weeks respectively in the lab-scale. In the plant, the remaining mass was 97.2% and 99.5%, much higher compared to the average of 68.9% after 3 weeks in the supplementary lab-scale test. The soft packaging samples (109±9 µm sample thickness) retained on average 45.4%, 10.9% and 0.3% of its mass after 4, 8 and 12 weeks respectively in the lab-scale. In the plant, a high remaining mass was also observed (94.0% and 93.8%). The supplementary lab-scale test showed similar remaining mass but higher fragmentation after 3 weeks. Conclusions: The results show that the samples achieved significant disintegration in the lab-scale but not in the plant. The difference between the tests that might further contribute to the differing degradation rates is the composition and heterogeneity of the composting substrate. Therefore, the substrate composition and thermophilic composting duration of individual plants are important considerations to determine the suitability of treating compostable plastic in real-world conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.