Abstract
To understand the mechanism of mass transfer during solid state reactions and order-disorder transitions the formation processes of CuAuI and L10-FePd ordered structures at solid state reactions in Cu/Au и Fe/Pd bilayer thin films have been carried out using the method of in situ electron diffraction (ED). The value of the long-range order (LRO) parameter has been estimated for the L10 type ordered structures being formed; the order-disorder transition temperatures have been determined. The formation mechanism of the L10 type ordered structures formed at the initial stages of the solid state reaction in the Cu/Au and Fe/Pd thin films has been suggested. In the case of Cu/Au it has been shown that the interdiffusion of copper and gold at the initial stage of the solid state reaction results in the reduced size of the grains of the initial materials, as a result, nanocrystalites of the Cu-Au solid solution are formed, and further, grains of the CuAuI ordered solid solution appear and their growth begins.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.